more mechanical questions

"Joshua Goldberg" skrev...

Quoted message said:

Okay...I am now virtually tool free (none left) and all I have left is to spread the rear triangle
of the trike about 1.5 inches (further/farther) apart than stock. I have no idea how to spread the
rear triangle (where the dropouts are). Question: if I used a Blow Torch to warm up the 4130 steel
and just used brute strength and pryed the sucker apart and stuck in the axle...ya think the frame
will crack when it gets cold again? There is some flex in the steel now, but not enough when the
steel is cold and I suspect brittle. Any ideas?

Heard of one who used the jack from his car and carefully spread it that way. Used it on the Zox
homebuilt.

Mikael

A Jack would work....good heavy iron, not possible for me to break
it...sounds good to me, will try that thanx.

"Mikael Seierup" <[email hidden]> wrote in message
"]news:[email hidden]...

Quoted message said:

"Joshua Goldberg" skrev...

Quoted message said:

Okay...I am now virtually tool free (none left) and all I have left is

to

Quoted message said:

Quoted message said:

spread the rear triangle of the trike about 1.5 inches (further/farther) apart than stock. I
have no idea how to spread the rear triangle (where the dropouts are). Question: if I used a
Blow Torch to warm up the 4130 steel and just used brute strength and pryed the sucker apart and
stuck in the axle...ya

think

Quoted message said:

Quoted message said:

the frame will crack when it gets cold again? There is some flex in the steel now, but not
enough when the steel is cold and I suspect brittle.

Any

Quoted message said:

Quoted message said:

ideas?

Heard of one who used the jack from his car and carefully spread it that

way.

Quoted message said:

Used it on the Zox homebuilt.

Mikael

"Joshua Goldberg" skrev...

Quoted message said:

A Jack would work....good heavy iron, not possible for me to break
it...sounds good to me, will try that thanx.

His website is here if you want to ask him about the specifics before trying.
hjem.get2net.dkmogens skovOpen ↗

Mikael

Any 41XX series steel must be cooled very slowly after heating, else it will become brittle and
break. (sometimes it will explode if cooled rapidly). If heated to red hot, (1100+ degrees F.) it
should be cooled over about an 8-10 hour period. Wrap the heat affected areas in a fiber glass
blanket and allow to sit over night, you might be able to use some of the pink ceiling insulation
without the paper backing.

"Joshua Goldberg" <[email hidden]> wrote in message
"]news:[email hidden]...

Quoted message said:

Okay...I am now virtually tool free (none left) and all I have left is to spread the rear triangle
of the trike about 1.5 inches (further/farther) apart than stock. I have no idea how to spread the
rear triangle (where the dropouts are). Question: if I used a Blow Torch to warm up the 4130 steel
and just used brute strength and pryed the sucker apart and stuck in the axle...ya think the frame
will crack when it gets cold again? There is some flex in the steel now, but not enough when the
steel is cold and I suspect brittle.

Any

Quoted message said:

ideas?

The Oracle seems to favour bending cold:

sheldonbrown.comframe spacing.htmlOpen ↗

Chris

"Joshua Goldberg" <[email hidden]> wrote in message
news:<[email hidden]>...

Quoted message said:

Okay...I am now virtually tool free (none left) and all I have left is to spread the rear triangle
of the trike about 1.5 inches (further/farther) apart than stock. I have no idea how to spread the
rear triangle (where the dropouts are). Question: if I used a Blow Torch to warm up the 4130 steel
and just used brute strength and pryed the sucker apart and stuck in the axle...ya think the frame
will crack when it gets cold again? There is some flex in the steel now, but not enough when the
steel is cold and I suspect brittle. Any ideas?

"derral" <[email hidden]> wrote in message news:<[email hidden]>...

Quoted message said:

Any 41XX series steel must be cooled very slowly after heating, else it will become brittle and
break. (sometimes it will explode if cooled rapidly). If heated to red hot, (1100+ degrees F.) it
should be cooled over about an 8-10 hour period. Wrap the heat affected areas in a fiber glass
blanket and allow to sit over night, you might be able to use some of the pink ceiling insulation
without the paper backing.

"Joshua Goldberg" <[email hidden]> wrote in message
"]news:[email hidden]...

Quoted message said:

Okay...I am now virtually tool free (none left) and all I have left is to spread the rear
triangle of the trike about 1.5 inches (further/farther) apart than stock. I have no idea how to
spread the rear triangle (where the dropouts are). Question: if I used a Blow Torch to warm up
the 4130 steel and just used brute strength and pryed the sucker apart and stuck in the
axle...ya think the frame will crack when it gets cold again? There is some flex in the steel
now, but not enough when the steel is cold and I suspect brittle.

Any

Quoted message said:

ideas?

I would NOT heat it (that's why they call it 'cold-setting). Get two 4' pieces of say 1"x4" plank.
Remove wheel, stand behind bike, slide planks together into r. triangle along line of chainstay. Now
pry'em apart. Stays will spread evenly. IMPORTANT: make sure the dropouts face each other squarely
if you don't want a lot of busted axles. Take two old axles and run the nuts in so they can each sit
in a dropout facing each other, kissing. Get them to line up! You should also check tracking by
running a thread from dropout-to-head-tube-to-dropout and measuring with calipers at whatever passes
for a seat tube in yr frame design. Don't pop any welds - Ъ×

Quoted message said:

it should be cooled over about an 8-10 hour period.

I assume you know a whole lot more about his metal than I do. Unless I knew different specifically,
I might have a tendency to think that heating it would cause/allow any dislocations in the metal
introduced when cold-worked at manufacturing time (which add strength and reduce ductility), to
'anneal'. This process allows the metal to re-form in a more relaxed state which yields a much
milder material with a great deal fewer dislocation in the atomic structure of the metal, which will
bend much easier. Like a coat-hanger that has been through a fire.

I sure wouldn't heat mine, but I am a newbie and I don't pretend to know all of the answers. Nor am
I wise enough to sit quietly till I do know the answers!

GeoB :-)

Prov 10:19 "When there are many words, trangression is unavoidable, but he who restrains his
lips is wise"

Right, the anneal process comes from heating and cooling at a slow rate. Cold working 41xx steel
will create a hard, brittle material. This material is used to manufacture oil drill string
components, it's not uncommon for the thread connections to harden to a Rockwell C scale of 45-50
after severe drilling conditions where there is a lot of flex in the drill string. These have to be
annealed back to about a 28-36 hardness to prevent breakage.

I was not advocating heating a bicycle frame, just stating what I know about what happens to
Chrome-Moly steel when it is heated.

"GeoB" <[email hidden]> wrote in message "]news:[email hidden]...

Quoted message said:

Quoted message said:

it should be cooled over about an 8-10 hour period.

I assume you know a whole lot more about his metal than I do. Unless I knew different
specifically, I might have a tendency to think that heating it would cause/allow any dislocations
in the metal introduced when cold-worked at manufacturing time (which add strength and reduce
ductility), to 'anneal'. This process allows the metal to re-form in a more relaxed state which
yields a much milder material with a great deal fewer dislocation in the atomic structure of the
metal, which will bend much easier. Like a coat-hanger that has been through a fire.

I sure wouldn't heat mine, but I am a newbie and I don't pretend to know all of the answers. Nor
am I wise enough to sit quietly till I do know the answers!

GeoB :-)

Prov 10:19 "When there are many words, trangression is unavoidable, but he who restrains his lips
is wise"

Okay Already Seems my Triangle was NOT my only problem. I did spread the triangle apart using the 2
Wood Plank suggestion (it worked well...thanks). Glitch #2 appeared, the Axle is 1/5th inch larger
in Diameter than are the dropouts and since I already fried my Dremel, am going to have to find a
metal file and widen the dropouts Thursday morning. Can it get any worse??...I have a box of these
new axles and every frame I tried appears to have dropouts too small....hmmm guess this is why the
axles were on sale. What is the line again about there being one new one being born every minute.
----------------------------------------------------------------------------
------------------------------
"derral" <[email hidden]> wrote in message "]news:[email hidden]...

Quoted message said:

Right, the anneal process comes from heating and cooling at a slow rate. Cold working 41xx steel
will create a hard, brittle material. This material is used to manufacture oil drill string
components, it's not uncommon for the thread connections to harden to a Rockwell C scale of

45-50

Quoted message said:

after severe drilling conditions where there is a lot of flex in the drill string. These have to
be annealed back to about a 28-36 hardness to prevent breakage.

I was not advocating heating a bicycle frame, just stating what I know

about

Quoted message said:

what happens to Chrome-Moly steel when it is heated.

"GeoB" <[email hidden]> wrote in message "]news:[email hidden]...

Quoted message said:

Quoted message said:

it should be cooled over about an 8-10 hour period.

I assume you know a whole lot more about his metal than I do. Unless I knew different
specifically, I might have a tendency to think that heating it would cause/allow any
dislocations in the metal introduced when cold-worked at manufacturing time (which add
strength and reduce ductility), to 'anneal'. This process allows the metal to re-form in a
more relaxed state which yields a much milder material with a great deal fewer dislocation in
the atomic structure of the metal, which will bend much easier. Like a coat-hanger that has
been through a fire.

I sure wouldn't heat mine, but I am a newbie and I don't pretend to know all of the answers. Nor
am I wise enough to sit quietly till I do know the answers!

GeoB :-)

Prov 10:19 "When there are many words, trangression is unavoidable, but he who restrains his
lips is wise"